Controlling Mechanical Properties of Ultra-fine WC-10%Co Cemented Carbides for Precision Molds 精密金型用超微粒WC-10%Co超硬合金の機械特性制御
Kenji FUJIMOTO 藤本賢二
Key words Hardness, transverse rupture strength, fracture toughness, inhibitor, grain growth
キーワード 硬さ,抗折力, 破壊靱性, 抑制剤, 粒成長

Abstract

Mechanical properties of ultra-fine cemented carbides for precision molds are affected by VC and Cr3C2 which are added to as grain-growth inhibitors. Therefore, the addition effects of VC and Cr3C2 on ultra-fine WC-10%Co cemented carbides were investigated. It was confirmed that on the basis of hardness, the grain growth-inhibiting effect score of Cr3C2 is 0.38 with a score of 1 representing VC. We also confirmed the influence of Cr3C2 on the transverse rupture strength and the fracture toughness is smaller than that of VC.
精密金型用超微粒超硬合金の機械的性質は粒成長抑制剤として添加されるVC とCr3C2 に大きく影響を受ける。そこでWC-10%Co 超微粒超硬合金におけるVC とCr3C2 の添加の影響を調査した。硬さを基準に VC の粒成長抑制効果を1 とした場合、C3C2 の粒成長抑制効果は0.38 であることが確認された。また、抗折力や破壊靱性値に及ぼすCr3C2 の影響はVC より小さいことを確認した。

詳細資料はこちらからご覧ください
← 前へ  | TOP | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |

日本タングステンへのお問い合わせはこちら

お電話・FAXのお客様はお近くの支店へお問い合わせください。
  • 東京支店 TEL 03-5812-2481 FAX 03-5812-2484
  • 名古屋支店 TEL 052-203-1081 FAX 052-203-1082
  • 大阪支店 TEL 06-6372-5681 FAX 06-6371-3986
  • 九州支店 TEL 0942-50-0050 FAX 0942-50-0055
日本タングステン株式会社(Nippon Tungsten Co.,Ltd)
〒812-8538 福岡市博多区美野島一丁目2番8号
TEL 092-415-5500(代表) / FAX 092-415-5511(代表)
Copyright(C) 2006 Nippon Tungsten Co., Ltd. All right reserved.
お問い合わせフォーム お電話・FAXでのお問い合わせ