Improvement of Product-life and Chippingresistance of a Cemented Carbide Rotary Cutter by Cemented Carbide-coated (CC) Anvil Roll超硬コーティングアンビルロール（CC アンビルロール）適用による超硬ロータリーカッターの寿命および耐チッピング性の向上
Yasutaka TSUJITA辻田泰隆
Key words
NT Die Cutter, rotary cutter, anvil roll, long life, wear resistance, chipping, high reliability
キーワード
NT ダイカッター, ロータリーカッター，アンビルロール, 長寿命，耐摩耗性，刃先チッピング, 高信頼性
Abstract
The NT Die Cutter consists of a die cutter having three dimensional cutter blades on the cylindrical outer surface and an anvil roll having a smooth cylindrical outer surface. NT Die Cutter is used all over the world as a cemented carbide rotary cutter for processing the outline of sanitary napkins and diapers at high speed. We developed “CC Anvil Roll”, an anvil roll which satisfies both a long operational lifetime and low risk of cutting edge chipping（Patent No. 5797408）. CC Anvil Roll (Cemented Carbidecoated Anvil Roll) has a thin hard layer and achieves a long operational lifetime due to the excellent wear resistance of it and reduces the risk of cutting edge chipping with its cushion performance making use of low Young's modulus of the base material. In this study, we conducted a running test with other materials and carried out a comparative evaluation of CC Anvil Roll based on its abrasion behaviors. As a result, it was confirmed that CC Anvil Roll has excellent wear resistance comparable to a cemented carbide anvil roll and reduces the risk of cutting edge chipping.
NT ダイカッターは外周上に刃先を形成するダイカッターと外周が平坦なアンビルロールからなり、ナプキンやおむつなどの高速輪郭加工用超硬合金製ロータリーカッターとして、Global 市場で広く使用されている。ダイカッターの長寿命化と刃先損傷のリスク低減を両立させるアンビルロールとして「CC アンビルロール」を開発した（特許5797408）。CC アンビルロール（超硬コーティングアンビルロール）はロール表面にWC-Co の薄い硬質層を有しており、それによる耐摩耗性と母材の低ヤング率を生かしたクッション性能で長寿命化と刃先損傷のリスク低減を実現する。本研究では他の材料とともに実機稼働試験を行い、その摩耗挙動からCC アンビルロールの効果を比較評価した。その結果、CC アンビルロールは超硬合金製アンビルロールに匹敵する優れた耐摩耗性を有しており、刃先チッピングのリスク低減効果も確認された。
詳細資料はこちらからご覧ください