技術情報

2006  Volume 38 

Effect of Oxygen Introduction on Oxidation Resistance, Oxygen Amountand Cutting Performance of Silicon Nitride Based Ceramics 窒化珪素基セラミックスの耐酸化性、酸素量、切削性能に及ぼす酸素導入の効果
Mituyoshi NAGANO, Hideaki SANO*, Shigeya SAKAGUCHI, Guo-Bin Zheng*, Yasuo UCHIYAMA* 永野 光芳、佐野 英明*、坂口 茂也、鄭 国斌*、内山 休男*
Key words Si3N4 ceramics, oxygen introduction, oxidation behavior, mechanical properties, wear resistance, cutting tool
キーワード 窒化珪素基セラミックス、酸素導入、酸化挙動、機械的性質、耐摩耗性、切削工具

Abstract

In order to clarify the wear resistance as cutting tools, the relationship between oxygen addition and cutting performances of the β-Si3N4 ceramics with 5 mass% Y2O3 and 2 or 4 mass% Al2O3 was investigated. From test results, we could conclude that the mechanical properties of β-Si3N4 ceramics depending on oxygen introduction are effective on cutting performance improvements of β-Si3N4 ceramics.

* Department of Materials Science and Engineering, Faculty of Engineering, Nagasaki University
 切削工具の耐摩耗性を検討するために、5mass%のY2O3と2または4mass%のAl2O3を添加したβ-Si3N4セラミックの切削性能と酸素添加量の関係を調査した。試験結果によれば、β-Si3N4セラミックの機械的性質は酸素の導入量により変化するので、β-Si3N4セラミック切削性能改良に有効であると結論づけられた。

* 長崎大学工学部材料工学科
← 前へ  | TOP | 1 | 2 | 3 | 4 | 5 |

日本タングステンへのお問い合わせはこちら

お電話・FAXのお客様はお近くの支店へお問い合わせください。
  • 東京支店 TEL 03-5812-2481 FAX 03-5812-2484
  • 名古屋支店 TEL 052-203-1081 FAX 052-203-1082
  • 大阪支店 TEL 06-6372-5681 FAX 06-6371-3986
  • 九州支店 TEL 0942-50-0050 FAX 0942-50-0055
日本タングステン株式会社(Nippon Tungsten Co.,Ltd)
〒812-8538 福岡市博多区美野島一丁目2番8号
TEL 092-415-5500(代表) / FAX 092-415-5511(代表)
Copyright(C) 2006 Nippon Tungsten Co., Ltd. All right reserved.
お問い合わせフォーム お電話・FAXでのお問い合わせ