組成の異なるp型CrSi2接合材料における、温度差を必要としない起電力の検証｜NippoTungstennn Review

2025 Volume 43

Verification of Electromotive Force in the Absence of a Temperature Difference in p-type CrSi2 Bonded Samples with Different Compositions 組成の異なるp型CrSi2接合材料における、温度差を必要としない起電力の検証

Takahiro ORITA, Kazuhiro ICHINO 折田昂優、一野和寛

Key words	CrSi2, thermoelectric material, Seebeck coefficient
キーワード	CrSi2，熱電材料，ゼーベック係数

This study examined the generation of an isothermal electromotive force in bonding materials consisting of CrSi2 and CrSi2-xAlx. The samples were prepared by hot-press sintering and analyzed in terms of crystal structure, Seebeck coefficient, and resistivity. The results indicated that the bonded samples exhibit a distinct interface devoid of Al diffusion, with a positively charged CrSi2 side and a negatively charged CrSi2-xAlx side. The electromotive force was observed to increase in proportion to the composition difference, peaking at approximately 400 °C.

本研究では，組成の異なるCrSi2およびCrSi2-xAlxからなる接合材料における等温起電力の発生について調べた．ホットプレス焼結を用いて試料を作製し，結晶構造，ゼーベック係数，抵抗率を分析した．その結果，接合試料はAl拡散のない明瞭な界面を持ち，均一加熱時にCrSi2側が正に，CrSi2-xAlx側が負に帯電する起電力が確認された．起電力は組成の差が大きいほど増加し，また，400℃付近でピークに達することが分かった．

5_verification_of_electromotive_foce_without_temperature_differrence_in_p-type_CrSi2_bonded_sample_with_different_compositions.pdf

← 前へ | TOP | 1 | 2 | 3 | 4 | 5 |

日本タングステンへのお問い合わせはこちら

お問い合わせフォーム

お電話、FAXでのお問い合わせ

お電話・FAXのお客様は
お近くの営業事務所へ
お問い合わせください。

東京事務所 TEL 03-5244-9266 ／ FAX 03-5244-9267
刈谷事務所 TEL 0566-45-5333 ／ FAX 0566-45-5334
大阪事務所 TEL 06-6152-8577 ／ FAX 06-6152-8614
基山事務所 TEL 0942-81-7760 ／ FAX 0942-81-7712
TEL 0942-50-0050 ／ FAX 0942-81-7713

日本タングステン株式会社(Nippon Tungsten Co.,Ltd)
〒812-8538 福岡市博多区美野島一丁目2番8号
TEL 092-415-5500(代表) / FAX 092-415-5511(代表)

2025 Volume 43

Abstract

日本タングステンへのお問い合わせはこちら